<h1>铝合金链轮固溶处理工艺改进</h1>
<div class="v2_comtent_info01">
<span>2013-12-13 8:59:39</span>来源：<span>中铝网</span>作者：<span></span>
</div>
<div class="v2_comtent_info02"><a title="投稿" class="v2_content_ico01">投稿</a><a title="打印" class="v2_content_ico02">打印</a><a title="收藏" class="v2_content_ico03">收藏</a>
<!-- Baidu Button BEGIN -->
<div id="bdshare" class="bdshare_t bds_tools get-codes-bdshare">
<span class="bds_more">分享到：</span>
<a class="bds_qzone"></a>
<a class="bds_tsina"></a>
<a class="bds_tqq"></a>
<a class="bds_renren"></a>
</div>
</div>
<script type="text/javascript" id="bdshare_js" data="type=tools&uid=684790" ></script>
<script type="text/javascript" id="bdshell_js"></script>
<script type="text/javascript">document.getElementById("bdshell_js").src = "http://bdimg.share.baidu.com/static/js/shell_v2.js?cdnversion=" + new Date().getHours();</script>
<!-- Baidu Button END -->
<div class="v2_comtent_info03">
<ul>
<li><b class="v2_content_ico04">导读：</b></li>
<li>链轮是自行车曲柄链轮总成的一个重要零件，该零件的加工工艺为：剪条料→落料→冲中心孔→成形→冲齿→砸齿→冲6-准25孔→固溶处理。</li>
</ul>
<ul>
<li><b class="v2_content_ico05">关键字：</b></li>
<li>铝合金 成本 链轮</li>
</ul>
<div class="clear_hu"></div>
</div>
<div class="over_x"><p><b>链轮</b>是自行车曲柄链轮总成的一个重要零件，该零件的加工工艺为：剪条料→落料→冲中心孔→成形→冲齿→砸齿→冲6-准25孔→固溶处理。</p>
<p>该零件的固溶处理工艺规范：温度495～503℃，保温时间15～20min，冷却介质为25～35℃水。零件经冲压加工后，零件平面度达到要求，但经固溶处理后，零件平面度都超过产品图的要求。为保证零件的技术要求，在固溶处理前，先采用螺栓和压板将链轮固定在专用挂具上，然后进行固溶处理。固溶处理后，卸下螺栓和压板，将链轮从专用挂具上取出，链轮的平面度仍不能满足产品图的要求。</p>
<p>采用水作为淬火介质，其优点是：操作简便、<b>成本</b>低廉、冷却快，能保证<b>铝合金</b>的性能要求。但从避免和减小工件变形的角度来讲，水又不是一种理想的淬火介质。由于冷却过快，工件表面和心部，以及不同壁厚之间出现很大的温差，引起相当高的内应力。在高温下，铝合金十分柔软，故极易造成变形;在低温下，内应力可能导致工件开裂。目前，在生产中，为减小工件变形，常采用提高水温的办法或用油淬、等温淬火等工艺，或采取聚合物作淬火介质。采用油淬，需要增加除油工序。而采用等温淬火工艺，工艺复杂。而采用聚合物作淬火介质，其优点是，冷却能力可通过改变浓度调整。低浓度聚合物水溶液的冷却速度和冷水相当，甚至更高，随浓度增加，冷却能力下降而接近油、热水。其次，成本高，生产管理不如水简便。</p>
<p>根据以上分析，决定采用100℃热水作为淬火介质。固溶处理工艺规范：温度495～503℃，保温时间15～20min。经上述工艺固溶处理后的链轮，平面度都小于0.26mm。<br />
</p>
<p>(关键字：铝合金 成本 链轮)</p></div>